High quality MgO board for sale
Date:2020-03-13 14:20:34 Author:
Subject
|
Item
|
Requirement
|
Standard
|
Color:
|
White
|
Diagonals
|
+/-2mm
|
Edge Square
|
|
Straightness of edges
|
1.5mm/M
|
Apparent Density
|
1050≤ρ≤1150kg/m3
|
Moisture Content
|
15-18% 12% after 28days
|
Bending Strength
|
18.8Mpa
10mm≥10mpa 28days JC 688-2006
|
Impacting Strength
|
8.3 kJ/m2 JC688-2006 Standard ≥2.0kJ/m2
|
Nailing strength
|
86N/ m2 JC688-2006 Standard ≥20 N/ m2
|
Water Permeability
|
No obvious moisture or water on the back
side
|
Percentage of dry shrinkage
|
≤0.3%
|
Percentage of water swelling
|
≤0.6%
|
Content of Chloride ion
|
≤3-6%
|
Dehalogenation Resistance
|
Temperature 32degrees, humidity 96degrees,
testing 72 hours, no water and no moisture created (qualified)
|
Environment
|
No Radiation, No Asbestos, No
formaldehyde
|
Alkali resistance on surface
|
No Abnormal Appearance on Surface
|
Fungal Growth Measurements
|
No Fungal Growth
|
Fireproof Performance
|
Following GB8624-1997 A-level
|
Edge
|
90°
|
Assist-Material
|
No Objectionable Ingredient, Industry
Rubbish, No Injurant wood dust, No venomousness item
|
Magnesium Oxide
|
Component
|
≥50% of total powder material
|
Content
|
≥85% Magnesium Oxide Material Content
|
Active of Magnesium Oxide
|
Active ≥65
|
Loss on Burning
|
Loss on Burning 5-6%
|
Granularity
|
≥200
|
Magnesium Chloride
|
Content
|
≥44.50%
≥44.50% Magnesium Chloride Material
Content
|
Other Chemical Composition
|
Sulfate ion≤2.80%;
Alkali metal chloride≤0.90%
|
Variety of Modifier
|
2 type will be use
|
name: 1:Polyvinyl alcohol
2:Coupling agent
|
Specially Item
|
|
Silicon Dioxide (20% of total powder material)
|
|
Small of(Alkali-resis) Fiber glass will add to mix material(15% of total powder of Mgo)
|
Fiber Glass Matting
|
Layer
|
2 layer
|
Size of Fiber Matting
|
Width: 1300mm Hole:4mmx4mm
|
Mass per unit area
|
150g/m2 -250 g/m2
|
Breaking Force
|
Each layer≥1600N/50mm
|
Alkali resistance of Retention rate
|
≥65%
|
Matting of Alkali Metal Oxides
|
≤12%
|
Perlite
|
Size
|
Even granulartity:1-2mm
|
Wood Dust
|
Size
|
60-80 less than 3mm
|
Matting
|
Mass per unit area
|
15g/m2
|